| CAS No.: | 9002-86-2 |
|---|---|
| Formula: | -(CH2-Chcl)N- |
| Environmental Protection: | Yes |
|
Still deciding? Get samples of US$ 10/kg
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
According to the different application scope, PVC can be divided into: universal PVC resin, high polymerization degree PVC resin, cross-linked PVC resin. General purpose PVC resin is formed by polymerization of vinyl chloride monomer under the action of initiator; High polymerization degree PVC resin refers to the resin which is polymerized by adding chain growth agent in the polymerization system of vinyl chloride monomer; Crosslinked PVC resin is a resin which is polymerized by adding crosslinker containing diene and polyene into vinyl chloride monomer polymerization system.
According to the method of obtaining vinyl chloride monomer, it can be divided into calcium carbide method, ethylene method and imported (EDC, VCM) monomer method (customary ethylene method and imported monomer method are called ethylene method).
According to the polymerization method, PVC can be divided into four categories: suspension polyvinyl chloride, emulsion polyvinyl chloride, bulk polyvinyl chloride and solution polyvinyl chloride. Suspension polyvinyl chloride is the largest variety of production, accounting for about 80% of the total production of PVC. Suspension polyvinyl chloride is divided into six models according to absolute viscosity: XS-1, XS-2... XS-6; XJ-1, XJ-2... , XJ-6. The meaning of each letter in the model: X-suspension method; S-loose type; J-compact type.
According to the plasticizer content, PVC plastic is often divided into: no plasticizer PVC, plasticizer content is 0; Rigid PVC, plasticizer content is less than 10%; Semi-rigid PVC, plasticizer content is 10-30%; Soft PVC, plasticizer content is 30-70%; Polyvinyl chloride paste plastic, plasticizer content of more than 80%
| Product Name | Suspension polyvinyl chloride resin S1300 |
Designation | ||
| Standard | Q/SH3160 77-2019 | Batch Number | ||
| Sampling location | 1#Packaging line | Sampling time | ||
| Item | Index | Inspection result | ||
| Superior | Qualified | |||
| Appearance | White powder | White powder | ||
| K-value | 72-70 | 70 | ||
| Average degree of polymerization | 1250-1350 | 1300 | ||
| Apparent density, g/ml | 0.45-0.52 | 0.5 | ||
| Volatile(including water content), % | ≤0.30 | 0.11 | ||
| 100g plasticizer absorption, g | ≥27 | 28.6 | ||
| VCM residue ug/g | ≤2.0 | 0.8 | ||
| Screenings250um sieve pore, % | ≤2.0 | 1.2 | ||
| Screenings63um sieve pore, % | ≥95 | 98 | ||
| Number of "fish eye", /400 cm² | ≤10 | 8 | ||
| Number of Impurity particles | ≤16 | 12 | ||
| Whiteness(160ºC,10min), % | ≥78 | 86.2 | ||
| Dry popular, min | Report value | 0.67 | ||